MEGAPOXY RMF
GAP FILLING EPOXY PASTE ADHESIVE FOR CIVIL ENGINEERING
USE
MEGAPOXY RMF is specially formulated non-sag epoxy filling paste
and adhesive. This easy to use two-part epoxy product sets after mixing
with excellent properties ideally suited for the following applications.
BONDING
Precast concrete articles
Grouting bolts
Natural stones
Bricks and ceramics
Metals
FILLING AND REPAIR
Concrete Pipes and Tanks
Fibreglass articles
Concrete floors and stairs
Concrete columns
Insitu formed concrete
ADVANTAGES
Simple 1 : 1 mix ratio
Creamy texture, blends easily
Non sag on vertical surfaces
Rapid setting
Adheres and cures under adverse conditions (cold and damp)
Good strength retention after prolonged immersion in water
Tensile and compressive strength superior to concrete
Very good chemical resistance

PRODUCT SPEClFICATlON
PART "A" PART "B"
Consistency Thixotropic paste Thixotropic paste
Colour White Black or Neutral
Flash Point Above 100°C Above 100°C

SURFACE PREPARATION
METALS Should be grit blasted to clean surface.
Mechanically abraded and degreased.
Wire brushing is not entirely satisfactory and gives
minimal adhesion only.

CONCRETE Should be free from grease and oil. If necessary, clean
with
industrial grade degreasing agent. Once clean, steps must
be taken to remove laitence; this is best done by using :
Mechanical abrasion
Acid etching - concentrated hydrochloric acid (muriatic
acid) 1:1 with water, and spreading 0.5 litre of this
mixture to each square metre. After the reaction has
ceased (about 10 minutes) the area is thoroughly washed
and scrubbed with a stiff bristled broom to remove loose
sand and allowed to dry for 24 hours.
PAINTED SURFACES :
Metals - a proprietary brand paint stripper should be used.
Concrete - the surface may be either flame cleaned or mechanically
abraded.
PROCESSING DATA
Mixing Ratio : 1 part resin to 1 part hardener by volume
Mixing : Mix until uniform grey or white
Working life at 25°C : 10 minutes
Minimum application temperature :5°C
Minimum Cure Time : 2 hours at 25°C
Full Cure Time : 2days at 25°C
IMPORTANT INORMATION
It is essential that the correct mixing ratio be used and that the Part "A"
and Part "B" are thoroughly mixed together before use. Inaccuracies
and poor mixing will result in lower physical properties of the cured
system and, if the error is sufficiently large, the system may not cure
satisfactorily and discolour on ageing.

CURED PROPERTIES (TYPICAL)

Maximum operating temperature : 70°C
Density : 1.45 kg per litre
Tensile Strength
Tensile Bond Strength
: 25 MPa
: 10 MPa
Compressive Strength : 80 MPa
Flexural Strength : 15 MPa
Coefficient of linear expansion : 60 mm/mm/°C x 10-6
Properly mixed Megapoxy RMF not stain or discolour white or light
coloured marble and ceramics.
AVAILABILITY
MEGAPOXY RMF available in 4 litre & 20 litre kits. Shelf life of
unopened kits is 2 years minimum. Product should be stored in cool
dry store.
CLEANING
Uncured Megapoxy PM can be removed with Megapoxy Thinners.
PRECAUTIONS
Avoid prolonged contact with skin. Wash affected areas with soap and
warm water. For further information refer to Bulletin No.100 and Safety
Data Sheet for Megapoxy RMF.